Tungsten Carbide Plates | High-Hardness Carbide Sheets Supplier

Product Name: Tungsten Carbide Sheet (also known as Tungsten Carbide Plate / Cemented Carbide Slab)

Material Composition: WC (Tungsten Carbide) + Co (Cobalt Binder), with optional Nickel-bonded grades for corrosion resistance

Hardness Range: HRA 88 – 92 (equivalent to HRC 75 – 82)

Density: 14.5 – 15.0 g/cm³ (depending on cobalt content grade)

Thickness Availability: 0.5mm – 100mm (customized upon request)

Width & Length: Max dimension up to 450mm x 450mm; smaller strips/blanks also available

Surface Finish Options: As-sintered (ground), Precision Ground (±0.01mm), or Mirror Polished (Ra ≤ 0.4μm)

Typical Grades: YG6, YG8, YG15, YG20, or equivalent ISO K10/K20/K30 grades

Key Properties: High wear resistance, excellent compressive strength, good impact toughness, and stable performance at high temperatures

Common Applications: Stamping dies, wear liners, cutting tool blanks, seal rings, nozzles, and armor panels

Custom Service: Non-standard sizes, chamfering, drilling, and grinding available upon request

INQUIRY NOW

Get a Quote

Category: Tungsten Carbide Strips, Plates and Bar

Description

Product overview

Tungsten carbide sheet plate is mainly used to make high-speed die and multi-station progressive die for punching copper, aluminum, stainless steel, cold-rolled sheet, EI sheet, SPCC, silicon steel sheet, hardware, standard parts, upper and lower punches, etc. It is also an excellent material for making high-temperature resistance parts, wear-resistant parts, anti-shielding parts, anti-radiation, and corrosion-resistant parts.

Main Process Flow:

Powder milling→ formula according to application requirements → wet milling → mixing → crushing → drying → sieving → adding forming agent → redrying → sieving to obtain cemented carbide powder→ granulating → pressing → forming → low-pressure sintering →blanks→Flaw inspection→Packing→Warehousing

Features:

High hardness for precision stamping
Excellent wear resistance for long die life
Good impact strength for high-volume production
Ideal for progressive and punching die applications

Technical specifications

Length (mm)	Width (mm)	Height (mm)
300	200	10～45
200	200	10～45
200	20	10～45
150	150	10～45
150	130	10～45
150	100	10～45
150	80	10~45
120	120	10～45
105	105	10～45
100	100	10～45
100	50	10～45
100	45	10～45
80	55	10～45
80	40	10～45
70	35	10～45
45	25	10～45
35	19	10～45
20	20	10~45
18	12	10～45

Note:

1.Advising HIP sintered for the plate which the thickness more than 10mm.

2.Before delivery to you, all plates were detected by no damage ultrasonice, keeping the plates all are no blister, no pore, high density & strength, impact resistance and long working life.

3.We can supply rough grinding or grinding the board surfaces.

Carbide grade

Grade	Dersity (g/cm)	Hardness (HRA)	T.RS (MPa)	Performance&application recommended
YG6A	14.85	92.5	2000	Fine grain alloy.good wear resistance.it is suitable for manufacturing forming cutter,wear-resistant parts etc.
YG8	14.7	89.8	2800	High bending strength,wear resistance lower than YG6A,suitable for manufacturing forming cutter,wear-resistant parts etc.
YG11	14.4	88.5	2900
YG15	14.0	87.0	3000	Suitable for manufacturing punching dies,wear-resistant parts eto.
YG20	13.5	85.5	2800	High bending strength,suitable for manufacturing progressive dies and other punching die5.
YG13X	14.2	90.0	3200
YS2T	14.25	92.0	2500	Fine grain alloy,with high wear resistance,bending strength,bonding resistance and thermal strength.It is suitable for machining refractory alloys,stainless steel,high manganese steel eto.